Description
| Chemical Composition: | In In present maximum unless indicated as a range or as a minimum | ||||||||||
| 8011 | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Each | Total | Aluminium |
| (% max) | 0.50-0.9 | 0.6-1.0 | 0.10 | 0.05 | 0.05 | 0.05 | 0.10 | 0.08 | 0.05 | 0.15 | Remainder |
| Typical Uses: | PP Caps; House Hold; semi-rigid containers. |
| Availability: | Coiled sheet only. Hot washed coil (with minimum residual oil) is available for 1.00 mm gauge and below only. |
| Tempers: | O, H14, H16 and H18. H12 and special tempers are subject to inquiry. |
| Mechanical Properties (Australian Standards) | |
| Temper | Gauge, | Tensile Strength, MPa | Elongation % | |
| mm | Minimum | Maximum | (50 mm L) | |
| O | 0.30-0.80 0.81-1.30 1.31-3.00 |
75 | 105 | 20 25 30 |
| H12 | Up to 0.50 0.51 to 0.80 0.81 to 1.30 1.31 to 3.00 |
100 | 135 | 3 4 6 8 |
| H14 | Up to 0.50 0.51 to 0.80 0.81 to 1.30 1.31 to 2.50 |
115 | 150 | 2 3 4 5 |
| H16 | Up to 0.50 0.51 to 0.80 0.81 to 1.30 1.31 to 2.00 |
140 | 170 | 1 2 3 4 |
| H18 | Up to 0.50 0.51 to 0.80 0.81 to 1.30 1.31 to 2.00 |
160 | – | 1 2 3 4 |
| Thickness (mm) | O” and H12 | 0.30~3.00 mm |
| H14 | 0.30~2.50 mm | |
| H16 | 0.30~2.00 mm | |
| H18 | 0.30~2.00 mm |
Thicknesses outside these limits are subject to inquiry.
| Width: | 870 – 1560 mm. (Narrower widths are subject to inquiry). |
| Arbors: | 300, 400, 508, 600 mm. |
| Annealing: | 340C± 5C, until all parts have reached the annealing temperature. Different temperatures and long soak times are often necessary to volatilize the foil rolling coolant present on the surface. |
| Weight Calculation: | kilogram per square meter = 2.71x thickness in mm. |